| Specific Gravity | 1.20 | 1.20 | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.00800 - 0.0100 cm/cm @Thickness 3.20 mm | 0.00800 - 0.0100 in/in @Thickness 0.126 in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.00800 -
0.0100 cm/cm @Thickness 3.20 mm | 0.00800 - 0.0100 in/in @Thickness 0.126 in | SABIC Method |
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Break | 150 % | 150 % | Type I, 50 mm/min; ASTM D 638 |
| Flexural Modulus | 1.96 GPa | 284 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Yield Strength | 82.0 MPa | 11900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 6.40 J/cm @Temperature -30.0 °C | 12.0 ft-lb/in @Temperature -22.0 °F | ASTM D 256 |
| 6.94 J/cm @Temperature 0.000 °C | 13.0
ft-lb/in @Temperature 32.0 °F | ASTM D 256 | |
| 8.01 J/cm @Temperature 23.0 °C | 15.0
ft-lb/in @Temperature 73.4 °F | ASTM D 256 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C @Thickness 6.40 mm | 230 °F @Thickness 0.252 in | unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0
°C @Thickness 6.40 mm | 194 °F @Thickness 0.252 in | unannealed; ASTM D 648 |